| Application: | Aviation, Electronics, Industrial, Medical, Chemical |
|---|---|
| Standard: | JIS, GB, DIN, BS, ASTM, AISI |
| Purity: | >99.95% |
|
Still deciding? Get samples of US$ 20/Piece
Request Sample
|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Specification:
| Type | Thickness | Length | Width | L1 | Depth |
| M-310 | 0.3 | 100 | 10 | 60 | 1.5-2.0 |
| M-215 | 0.2 | 100 | 15 | 60 | 1.5-2.0 |
| M-315 | 0.3 | 100 | 15 | 60 | 1.5-2.0 |
| M-515 | 0.5 | 100 | 15 | 60 | 1.5-2.0 |
| M-218 | 0.2 | 100 | 8 | 60 | 1.5-2.0 |
| M-312 | 0.3 | 100 | 12 | 60 | 1.5-2.0 |
| M-251 | 0.2 | 50 | 10 | 25 | 1.5-2.0 |
| M-353 | 0.3 | 50 | 13 | 25 | 1.5-2.0 |
| M-220 | 0.2 | 102 | 15 | 40 | 5.0 |
| M-223 | 0.2 | 100 | 23dia | 15 | 1.5-2.0 |
| Type | Name | Chemical Component | Application |
| Texture | Mo boat | Mo≥99.95% | It can reach 1100 degrees or so when under the high-temperature. As the melting smelting container of rare earth material |
| MoLa boat | La:0.4-1.2% Mo: remain |
It can reach 1700 degrees to 2000 degrees when under the high-temperature,high-temperature in the recrystallization temperature, it is not easy to become fragile for a long time | |
| TZM alloy boat | Ti:0.4-0.6% Zr:0.07-0.12% C:0.01-0.05% |
The highest operating temperature is1800ºC, have high intensity and good abrasion resistance |
| Shape | Plane | Suitable for high wettability material |
| "V" | Suitable for low wettability | |
| Oval | Suitable for the molten state of the material | |
| spherical | Expensive materials such as gold and silver | |
| Narrow | Prevent the filament clip[ from evaporation materials | |
| Aluminizing | It is helpful against the fused materials which have good corrosion resistance with plating a layer of alumina on the boat body surface |